PHYSICAL, MECHANICAL AND TECHNOLOGICAL SPECIFICATIONS |
|||||
Burdur Beige |
Toros Siyah |
Beysehir Beyaz |
Afyon Grey |
Aksehir Siyah |
|
| Hardness (Mohs) | 4,5 |
3-4 |
3 |
4 |
|
| Unit Volume By Weight (gr/cm3) | 2,67 |
2,71 |
2,73 |
2,71 |
|
| Density (gr/cm3) | 2,72 |
2,73 |
2,75 |
2,72 |
|
| Water Absorption at Atmospheric Pressure (by weight %) | 0,1 |
0,074 |
0,1 |
0,1 |
|
| (By Volume %) | 0,4 |
0,202 |
0,2 |
0,4 |
|
| Water Absorption at Boiling Water (by weight %) | 0,2 |
0,40 |
0,1 |
0,1 |
|
| (By Volume %) | 0,5 |
0,109 |
0,2 |
0,4 |
|
| Porosity (%) | 0,4 |
0,202 |
0,2 |
0,4 |
|
| Compressive Strength (kgf/cm2) | 1,120 |
1,382 |
701 |
807 |
|
| Compressive Strength After Freezing (kgf/cm2) | 1,125 |
1,144 |
590 |
657 |
|
| Strength to Blow (kgf.cm/cm3) | 2 |
17,9 |
23 |
15 |
|
| Strength to Bending (kgf/cm2) | 72 |
146 |
151 |
145 |
|
| Moduls of Elasticity (kgf/cm2) | 47,9x10^4 |
171,581 |
5,9x10^4 |
60,9x10^4 |
|
| Ration of Fullness (%) | 98,2 |
99,3 |
99,03 |
99,6 |
|
| Degree of Pores (%) | 1,8 |
0,7 |
0,7 |
04 |
|
| Average Abrasion Strength (cm3/50 cm2) | 14,70 |
19 |
25,4 |
24,7 |
|
| Average Tensile Strength (kgf/cm2) | 653 |
68 |
39 |
40 |
|
| CHEMICAL ANALYSIS (%) | |||||
| SiO2 | 0,15 |
2,56 |
0,24 |
0,49 |
|
| Fe2O3 | 0,15 |
0,51 |
0,02 |
0,30 |
|
| CaO | 55,60 |
49,97 |
49,53 |
55,40 |
|
| MgO | 0,25 |
2,07 |
2,21 |
Trace |
|
PHYSICAL, MECHANICAL AND TECHNOLOGICAL SPECIFICATIONS |
|||||
Burdur Kahve |
Teos Yesil |
Elazig Visne |
Baliskesir Sultan |
Akhisar Kirmizi |
|
| Hardness (Mohs) | 3,4 |
3 |
|||
| Unit Volume By Weight (gr/cm3) | 2,70 |
2,61 |
|||
| Density (gr/cm3) | 2,71 |
2,72 |
|||
| Water Absorption at Atmospheric Pressure (by weight %) | 0,2 |
0,75-0,99-1,91 |
|||
| (By Volume %) | 0,6 |
1,98-2,63-5,10 |
|||
| Water Absorption at Boiling Water (by weight %) | 0,2 |
1,12-1,48-2,86 |
|||
| (By Volume %) | 0,5 |
2,86-3,78-7,30 |
|||
| Porosity (%) | 0,6 |
3,2 |
|||
| Compressive Strength (kgf/cm2) | 1019 |
1019 |
|||
| Compressive Strength After Freezing (kgf/cm2) | 1019 |
521 |
|||
| Strength to Blow (kgf.cm/cm3) | 10 |
10 |
|||
| Strength to Bending (kgf/cm2) | 130 |
84 |
|||
| Moduls of Elasticity (kgf/cm2) | 4,12x10^4 |
6,65x10^4 |
|||
| Ration of Fullness (%) | 99,6 |
96,0 |
|||
| Degree of Pores (%) | 0,4 |
4,0 |
|||
| Average Abrasion Strength (cm3/50 cm2) | 16,7 |
29,4 |
|||
| Average Tensile Strength (kgf/cm2) | 71 |
67 |
|||
| CHEMICAL ANALYSIS (%) | |||||
| SiO2 | 1,27 |
28,35 |
|||
| Fe2O3 | 0,77 |
9,70 |
|||
| CaO | 53,50 |
13,75 |
|||
| MgO | 0,53 |
26,25 |
|||
|